Abstract This in vitro study evaluated the effect of an experimental varnish containing 20% nano-hydroxyapatite (nHAP) associated with 5% stannous chloride (SnCl2) against erosive-abrasive wear on bovine dentin. Samples of bovine cervical dentin were pre-eroded (0.3% citric acid, pH 2.6 for 10 minutes) and randomized into 4 groups (n=10): Control group - experimental varnish without active ingredient (CG); experimental varnish containing 20% nHAP (nHG); experimental varnish containing 5% SnCl2 (24.800 ppm Sn2+) (SnG); experimental varnish containing 20% nHAP associated with 5% SnCl2 (18.300 ppm Sn2+) (nHSnG). After applying the materials, the erosive-abrasive challenges were performed for five days. Erosive dentin loss and analysis of the pattern of dentinal obliteration were performed by 3D confocal laser microscopy. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The SnG and nHSnG experimental groups presented more effectiveness in preventing erosive wear when compared to the other groups (p<0.05). There was no statistically significant difference between the SnG and nHSnG groups (p = 0.731) in tooth structure dentin loss. Regarding the amount of open dentinal tubules, the highest amount of obstructed dentinal tubules was demonstrated in SnG and nHSnG (p < 0.05) when compared to the others. Between SnG and nHSnG there was no significant difference (p = 0.952) in the amount of closed dentinal tubules in the dentin. Experimental varnishes containing 5% SnCl2 associated or not with 20% nHAP showed to be a promising strategy in preventing erosive-abrasive wear of dentin. In addition, nHSnG was able to obliterate dentinal tubules.

Resumo Este estudo in vitro avaliou o efeito de um verniz experimental contendo 20% de nano-hidroxiapatita (nHAP) associado a 5% de cloreto estanoso (SnCl2) contra o desgaste erosivo-abrasivo da dentina bovina. As amostras de dentina cervical bovina foram pré-erodificadas (0,3% de ácido cítrico, pH 2,6 durante 10 minutos) e aleatorizadas em 4 grupos (n=10): Grupo controle - verniz experimental sem ingrediente ativo (GC); verniz experimental contendo 20% nHAP (GnH); verniz experimental contendo 5% SnCl2 (24.800 ppm Sn2+) (GSn); verniz experimental contendo 20% nHAP associado a 5% SnCl2 (18.300 ppm Sn2+) (GnHSn). Após a aplicação dos materiais, os desafios erosivo-abrasivos foram realizados durante cinco dias. Perda de dentina erosiva e análise do padrão de obliteração dentinária foram realizadas por microscopia laser confocal 3D. Foi realizado o teste ANOVA/Bonferroni unidireccional para analisar os dados (α=0,05). Os grupos experimentais GSn e GnHSn apresentaram maior eficácia na prevenção do desgaste erosivo quando comparados com os outros grupos (p<0,05). Não houve diferença estatisticamente significativa entre os grupos GSn e GnHSn (p = 0,731) na perda de dentina da estrutura dentária. Relativamente à quantidade de túbulos dentinários abertos, a maior quantidade de túbulos dentinários obstruídos foi demonstrada em GSn e GnHSn (p < 0,05) quando comparada com os outros grupos. Entre GSn e GnHSn, não houve diferença significativa (p = 0,952) na quantidade de túbulos dentinários fechados na dentina. Os vernizes experimentais contendo 5% de SnCl2 associados ou não a 20% de nHAP mostraram ser uma estratégia promissora na prevenção do desgaste erosivo-abrasivo da dentina. Além disso, o GnHSn conseguiu obliterar os túbulos dentinários.